Intamsys PolyMax 1.75mm 750g Filament
Intamsys PolyMax 1.75mm 750g Filament
Description
Brand：Polymaker
Extremely Tough
Featuring increased impact strength of up to times that of regular PLA and 20% better than ABS PolyMax PLA is a sure winner when it comes to toughness
Warp-Free
Have you finished a large part,Only to find that the part has warped to a point that it looks nothing like the original model? With PloyMax PLA you can print any part any size without the worry of warping,No heated bed or enclosed printing chamber required
ABS? NO More
With PolyMax PLA you can now get rid of that potentially hazardous ABS and still achieve the same structral strength,with better printer compatibility and safer experience with odour free printing
Jam-Free
Out patented Jam-Free technology dramatically improves the heat stability of PLA filaments by raising the softening temperature ensuring a worry free printing experience
Colourful
Brighten up your models with a choice of ten vibrant true colours,You are bound o find the right one for you
Uncompromised Quality
With our eight step Quality control process and rigorous in-house testing,you can reset assured that PolyMax PLA will produce beautiful,reliable and accurate printed parts every time
Physical Properties
| Property | Testing Method | Typical Value |
|---|---|---|
| Density(g/m³ at 21.5°C) | ASTM D792(ISO 1183,GB/T 1033) | 1.17-1.24 |
| Melt index(g/10min) | 190°C,2.16kg | 5-8 |
Â
Mechanical Properties
| Property | Testing Method | Typical Value |
|---|---|---|
| Tensile strength(MPa) | ASTM D638(ISO 527,GB/T 1040) | 28.1±1.3 |
| Elongation At Break(%) | ASTM D638(ISO 527,GB/T 1040) | 1.36±0.30 |
| Bending strength(Mpa) | ASTM D790(ISO 178,GB/T 9341) | 48.0±1.9 |
| Impact strength(KJ/m² | ASTM D256(ISO 179,GB/T 1043) | 12.15±1.30 |
Â
Testing Geometries
Â
Additional information
| Density |
1.17-1.24g/m³ |
|---|---|
| Melt Flow Index(g/10min) |
5-8(190°C/2.16kg) |
| Tensile Strength |
28.1±1.3MPa |
| Elongation At Break |
1.36±0.30% |
| Bendling Strength |
2119±60Mpa |
Â